Zirconium Silicate Beads PV:3120
-
Category:Zirconium Silicate
SPEC:0.4-5.0mm
Packaging:Bag Package/Small Bag Package
Zirconia ceramic grinding beads/ball is used as high class grinding media. Thanks to the extremely low wear loss, the zirconia based ceramic beads/ball is contamination free grinding media. Its widely used in various industries like medicine, food, cosmetics, paints, textiles,Structural Ceramics, Electronics Ceramics, Magnetic material, Metallurgy, printing and dyeing, pigment etc.
Application of Zirconia grinding Beads /ball:
Paint,pigment,coating,inks,electronic materials, magnetic materials.ceramic glaze,cosmetic etc.
Application of Zirconium silicate beads:
1.Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and other minerals;
2. Dielectric materials, piezoelectric materials, capacitor;
3. Ceramic glazes and frits;
4. Coatings, paints, inks etc;
5. Metallic minerals like copper, silver, nickel, gold, zinc etc;
6. Recommend to be used in stirred mill and ball mill.
Application:
Paint,pigment,coating,inks,electronic materials, magnetic materials.ceramic glaze,cosmetic etc.
Index | Unit | Contents |
ZrO2 | % | 94.6 |
Y2O3 | % | 5.4 |
Al2O3 | % | <0.3 |
Density | g/cm³ | 5.95-6.0 |
Hardness(HV) | GPa | >11 |
Bending Strength | MPa | >1150 |
Fracture Toughness | Mpa.m0.5 | 7-10 |
Grain size | μm | <0.5 |
Modulus Elasticity | GPa | 205 |
Abrasion | ppm/h | <5 |
Thermal conductivity | W/(m.k) | 3 |
Thermal Expansion Coefficient | X10-6/k | 11 |
Crush Strength | KN | ≥20(Ø6 for example) |
Filling Density | Kg/L | 3.5(Ø5 for example) |
Appearance | / | Shining,white, no porous, no crackle |